CEA Z Serie Manual De Instrucciones página 27

13. Suggestions for welding parameters
Our machines are usually supplied equipped for welding of iron sheets.
To obtain good welding results we suggest you to keep the following prescription:
13.1 Welding of sheet iron
Thickness
s
[mm]
0,25
0,5
0,75
1
1,25
1,5
2
2,5
3
Thickness
s
[mm]
0,25
0,5
0,7
1
1,25
1,5
2
2,5
3
Thickness
s
[mm]
0.25
0.5
0.75
1
1.25
1.5
2
2.5
3
D
d
30˚
Welding class A
D A
d
≥ ≥ ≥ ≥ ≥ min.
4 10 6,5
5 10 10
6 13 13
6,5 13 19
6,5 13 22
6,5 13 27
8 16 35
8 16 41
10 16 50,8
Welding class B
D A
d
≥ ≥ ≥ ≥ ≥
min.
4 10 6,5
5 10 10
6 13 13
6,5 13 19
6,5 13 22
6,5 13 27
8 16 35
8 16 41
10 16 50,8
Welding class C
D A
d
≥ ≥ ≥ ≥ ≥
min.
4 10 6,5
5 10 10
6 13 13
6.5 13 19
6,5 13 22
6,5 13 27
8 16 35
8 16 41
10 16 50,8
L
A
Welding Electrode
L
time force
min.
(periods) (daN)
10 3 91
11 5 136
12 6 181
13 9 227
14 10 295
16 12 362
17 18 496
19 21 590
22 25 815
Welding Electrode
L
time force
min.
(periods) (daN)
10 4 59
11 8 91
12 12 125
13 17 163
14 20 186
16 24 227
17 30 293
19 36 358
22 50 516
Welding Electrode
L
time force
min.
(periods) (daN)
10 13 29
11 18 45
12 24 61
13 31 81
14 35 93
16 40 113
17 48 147
19 55 177
22 65 259
ENGLISH
s
s
Welding Nugget
current diameter
(A) (mm)
4000 3,3
6100 4,3
8000 5,3
9200 5,8
10300 6,3
11600 6,9
13300 7,9
14700 8,6
17500 10,2
Welding Nugget
current diameter
(A) (mm)
3700 3,2
5100 4,1
6300 5,1
7500 5,6
8000 5,8
9000 6,6
10400 7,6
11400 8,4
12900 9,9
Welding Nugget
current diameter
(A) (mm)
3000 2,8
3800 3,5
4700 4,6
5600 5,3
6100 5,6
6800 6,4
7900 7,1
8800 7,9
10000 9,4
27