Composition; Technical Specifications - DENTSPLY Crypton Instrucciones Para El Uso

3 Composition

All figures in % w/w:
Co Cr Mo Mn
63.3 28.5 6.0 <0.8

4 Technical specifications

The following information applies after dense sintering in
a Crypton sintering furnace:
Type
Vickers hardness
0.2% yield strength
Tensile strength
Modulus of elasticity
Elongation at fracture
Density
Solidus
Liquidus
CTE (25 – 500°C)
(25 – 600°C)
g: sintered
b: Achievable values after ceramic veneering
Measurements performed on samples pursuant to EN ISO 22674
Si Fe N
<0.8 <0.3 <0.3
NEM bonding alloy
235 HV 10
g) 495 MPa
b) 480 MPa
g) 850 MPa
b) 820 MPa
b) 165 GPa
g) 22 %
b) 19 %
7,9 g/cm
3
1 360 °C
1 400 °C
14,7 µm/m·K
15,0 µm/m·K
Crypton for inLab | 12
®